SIGMAZINC 158

SIGMA VIKOTE 15

High-build, aluminum pigmented chlorinated rubber  primer/sealer   PRINCIPAL CHARACTERISTICS

• Anticorrosive primer/sealer
• Excellent water resistance
• Unsaponifiable
• Resistant to well designed/controlled cathodic protection
• Fast-drying
• Can be applied at low temperatures, down to –10°C (14°F)
• Tolerates a DFT up to 150 µm (6.0 mils) at overlaps without sagging
• Compatible with antifoulings

• Alu light – Gray
• Eggshell

SIGMASHIELD 460

Two-component, high solids glass flake reinforced polyamine adduct epoxy   coating   PRINCIPAL CHARACTERISTICS

• Excellent abrasion and impact resistance
• Suitable for use on ice-going vessels
• Excellent resistance to corrosion
• Long-term protection at areas subject to heavy wear and tear
• Resistant to splash and spillage of a wide range of chemicals
• Very low water permeability, due to glass flake barrier

• Black (other (light) colors on request)
• Gloss

SIGMAGUARD 750

Two-component, moisture-curing zinc-rich (ethyl) silicate  coating  

PRINCIPAL CHARACTERISTICS

• Tank coating with excellent solvent and chemical resistance
• To be used as tank coating or as a system primer in various paint systems based on unsaponifiable binders
• Can withstand substrate temperatures from –90°C (–130°F) up to 400°C (750°F), under normal atmospheric exposure conditions
• High zinc content resulting in excellent corrosion protection
• Good impact and abrasion resistance
• Certificate for ASTM A-490 class 'B' for slip coefficient
• Recognized corrosion control coating (Lloyd's register)
• Must not be used for immersion in alkaline (more than pH 9) or acidic (less than pH 5.5) liquids
• Complies with SSPC-Paint 20 level 2 and ISO 12944.5

SIGMACOVER 525

Two-component, polyamine-cured epoxy tie coat   PRINCIPAL CHARACTERISTICS

• Final coat in epoxy underwater anticorrosive systems
• Epoxy tie coat for use with PPG antifoulings as specified
• Excellent water resistance
• Good abrasion- and impact resistance

• Black, gray
• Flat